COURANTS CRITIQUES ET EPINGLAGE DU FLUX DANS LES FILS SUPRACONDUCTEURS HAUTE TEMPERATURE, STABILISES A L'ARGENT.

CRITICAL CURRENTS AND FLUX PINNING IN SILVER STABILIZED HIGH CRITICAL TEMPERATURE SUPERCONDUCTOR WIRES.

Auteurs : TENBRINK J., HEINE K., KRAUTH H.

Type d'article : Article

Résumé

PREPARATION DE FILS SUPRACONDUCTEURS EN YBACUO(7-) ET E BI(2)SR(2)CA(1)CU(2)O(8-), SOUS ARGENT, PAR LA TECHNIQUE DU TUBE DE POUDRE. CARACTERISATION DES ECHANTILLONS PAR MESURE DES DENSITES DE COURANT CRITIQUE A 77 K ET A 4,2 K ET PAR MESURE DE LA SUSCEPTIBILITE EN COURANT ALTERNATIF. ALORS QUE LA DENSITE DE COURANT CRITIQUE EST LIMITEE, DANS LES FILS D'YBCO/ARGENT, PAR LES LIAISONS FAIBLES, IL N'Y A PRATIQUEMENT PAS DE LIAISON FAIBLE DANS LES COMPOSES A BASE DE BISMUTH. A 4,2 K, IL EST POSSIBLE D'ATTEINDRE DES DENSITES DE COURANT CRITIQUE DE 57.000 A/CM2 EN CHAMP NUL ET DE 15.000 A/CM2 SOUS CHAMP DE 26 T, CE QUI PERMET D'UTILISER CE MATERIAU POUR LES APPLICATIONS SOUS CHAMP INTENSE. COMPARAISON DE CES RESULTATS AVEC CEUX OBTENUS POUR LES FILS SUPRACONDUCTEURS EN NIOBIUM-TITANE.

Détails

  • Titre original : CRITICAL CURRENTS AND FLUX PINNING IN SILVER STABILIZED HIGH CRITICAL TEMPERATURE SUPERCONDUCTOR WIRES.
  • Identifiant de la fiche : 1991-1987
  • Langues : Anglais
  • Source : Cryogenics - vol. 30 - n. 5
  • Date d'édition : 1990

Liens


Voir d'autres articles du même numéro (13)
Voir la source

Indexation