Dynamiques d'adsorption de revêtements en structure organométallique (MOF) pour le refroidissement entraîné par la chaleur perdue.

Adsorption dynamics of MOF coatings for waste heat driven cooling.

Numéro : pap. n. 1669

Auteurs : LAURENZ E., VELTE A., KUMMER H., et al.

Résumé

Adsorption chillers are a promising option for environmentally friendly data centre cooling allowing for high energy efficiency. Waste heat from liquid cooled CPUs (~60 °C) drives the cooling for auxiliary loads (~20 °C) with heat rejection around 30 °C. Adsorption properties of the metal-­organic frame work (MOF) aluminium fumarate largely outperform the state-­of-­the-­art material silica gel at these temperatures. With adsorbent coatings, volume and mass specific cooling power may be increased to reduce specific costs.
Samples were prepare with a binder-­based aluminium fumarate coating in three different thicknesses (140–610 µm) and measured for adsorption dynamics with large-­temperature-­jump-­experiments. Uptake-­times (15-­85%) are in the range of 9–78 s. On a full scale heat exchanger expected volume and adsorbent mass specific cooling powers are 200–700 W l-­1 and 1.3–14 kW kg-­1 – an increase to state-­of-­the-­art of 3–10 times and >10 times at reasonable cooling COPs of 0.47–0.57.

Documents disponibles

Format PDF

Pages : 8

Disponible

  • Prix public

    20 €

  • Prix membre*

    Gratuit

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : Adsorption dynamics of MOF coatings for waste heat driven cooling.
  • Identifiant de la fiche : 30026763
  • Langues : Anglais
  • Source : Proceedings of the 25th IIR International Congress of Refrigeration: Montréal , Canada, August 24-30, 2019.
  • Date d'édition : 24/08/2019
  • DOI : http://dx.doi.org/10.18462/iir.icr.2019.1669
  • Notes :

    Keynote


Liens


Voir d'autres communications du même compte rendu (632)
Voir le compte rendu de la conférence

Indexation