FISSURATION PAR CORROSION A LA CONTRAINTE DES ACIERS DANS L'AMMONIAC.

STRESS CORROSION CRACKING OF STEELS IN AMMONIA.

Auteurs : CRACKNELL A.

Type d'article : Article de périodique

Résumé

LA RUPTURE SE PRODUIT LORSQUE L'ACIER SUBIT UNE CONTRAINTE DEPASSANT SA RESISTANCE ELASTIQUE. LES PRODUITS FORTEMENT CORROSIFS REDUISENT EVIDEMMENT L'EPAISSEUR DE L'ACIER, PROVOQUANT AINSI L'APPARITION DE CONDITIONS DE DEFORMATION, MAIS CERTAINS PRODUITS FAIBLEMENT CORROSIFS SEMBLENT ABAISSER REELLEMENT LA RESISTANCE ELASTIQUE A CERTAINS POINTS, NOTAMMENT LA OU DES CONTRAINTES LOCALES ELEVEES SE PRODUISENT A DES ENDROITS TELS QUE LES SOUDURES OU LES COUDES. CES PRODUITS CORROSIFS DEPENDENT DU METAL ET LORSQU'IL S'AGIT D'ACIERS AU CARBONE L'AMMONIAC CONTAMINE PAR L'OXYGENE PEUT PROVOQUER DES PROBLEMES. QUELQUES ESSAIS DE LABORATOIRE INDIQUENT QUE LA PRESENCE D'EAU PEUT INHIBER CET EFFET, MAIS LES RESULTATS PRATIQUES AMENENT A DOUTER DE LEUR VALIDITE. LE DEFAUT EST TRES SUSCEPTIBLE DE SE PRODUIRE SUR LES COMPOSANTS DU COTE HAUTE PRESSION, MAIS LES CAS RAPPORTES SONT PEU NOMBREUX. LA PLUPART DES PROBLEMES SIGNALES SE SONT PRODUITS DANS ONIAC. D.W.H.

Détails

  • Titre original : STRESS CORROSION CRACKING OF STEELS IN AMMONIA.
  • Identifiant de la fiche : 1983-0303
  • Langues : Anglais
  • Source : Inst. Refrig., Adv. Proof - 4 p.; 1 fig.; 1 tabl.; 9 ref.
  • Date d'édition : 06/05/1982