INFLUENCE DE LA VALEUR DU RAPPORT DES CONCENTRATIONS BISMUTH/PLOMB ET DE LA TEMPERATURE DE RECUIT SUR LA TEMPERATURE CRITIQUE ET SUR LA FORMATION D'UNE PHASE SUPRACONDUCTRICE A HAUTE TEMPERATURE CRITIQUE, DANS BSCCO CONTENANT DU PLOMB EN SUBSTITUTION.

EFFECT OF BISMUTH/LEAD RATIO AND ANNEALING TEMPERATURE ON CRITICAL TEMPERATURE AND FORMATION OF HIGH-CRITICAL TEMPERATURE PHASE IN LEAD SUBSTITUTED BSCCO SUPERCONDUCTOR.

Type d'article : Article

Résumé

ETUDE DE L'INFLUENCE DE LA VALEUR DU RAPPORT DES CONCENTRATIONS BISMUTH/PLOMB ET DE LA TEMPERATURE DE RECUIT SUR LA TEMPERATURE CRITIQUE ET SUR LA FORMATION DE LA PHASE SUPRACONDUCTRICE A HAUTE TEMPERATURE CRITIQUE, PAR LE PROCEDE DE REACTION A TROIS ETAPES. LES VALEURS OPTIMALES SONT DE L'ORDRE DE 1,8/0,3 POUR LE RAPPORT DES CONCENTRATIONS BISMUTH/PLOMB ET DE 1108-1118 K (845-855 DEG C) POUR LA TEMPERATURE DE RECUIT. LA TEMPERATURE DE TRANSITION SUPRACONDUCTRICE DE LA PHASE HAUTE TEMPERATURE CRITIQUE ETUDIEE DECROIT LORSQUE LA TEMPERATURE DE RECUIT CROIT, BIEN QUE CETTE PHASE SOIT ISOMORPHE DE LA PHASE A 110 K.

Détails

Titre original : EFFECT OF BISMUTH/LEAD RATIO AND ANNEALING TEMPERATURE ON CRITICAL TEMPERATURE AND FORMATION OF HIGH-CRITICAL TEMPERATURE PHASE IN LEAD SUBSTITUTED BSCCO SUPERCONDUCTOR.
Identifiant de la fiche : 1992-0984
Langues : Anglais
Source : J. Supercond. - vol. 3 - n. 4
Date d'édition : 12/1990
Document disponible en consultation à la bibliothèque du siège de l'IIF uniquement.

Liens

Voir d'autres articles du même numéro (4)
Voir la source

Indexation

Thèmes : Supraconduction
Mots-clés : Supraconduction; Oxyde; Cuivre; Céramique; Calcium; BSCCO; Plomb; Bismuth; Température critique; Supraconducteur; Strontium; Haute température