STRUCTURE ET SUPRACONDUCTIVITE DES CERAMIQUES BISMUTH -(PLOMB)-CALCIUM-STRONTIUM-CUIVRE-OXYGENE OBTENUES PAR FUSION A L'ARC.

STRUCTURE AND SUPERCONDUCTIVITY OF BISMUTH-(LEAD)-CALCIUM-STRONTIUM-COPPER-OXYGEN CERAMICS PROCESSED BY ARC MELTING.

Auteurs : ALDICA G.

Type d'article : Article

Résumé

CES CERAMIQUES, DE COMPOSITION TYPIQUE EN CATIONS, PREFRITTEES A 1.073 K (800 DEG C) SONT OBTENUES PAR FUSION A L'ARC ET TREMPE RAPIDE DE LA PHASE SUPRACONDUCTRICE 2021, OXYDE DE CALCIUM ET OXYDE DE CUIVRE. LES ECHANTILLONS FRITTES DANS L'AIR A 1.113 K (840 DEG C)AVANT FUSION PRESENTENT UN CHANGEMENT DE PHASE SOLIDE ET UN MELANGE DES PHASES SUPRACONDUCTRICES 2122 ET 2223. LORSQU'ON UTILISE LA FUSION A L'ARC, ON OBSERVE UNE AUGMENTATION IMPORTANTE DE LA DENSITE (DE 3,7 A 5,7 G/CM3 ) ET DE LA DENSITE DE COURANT CRITIQUE (DE 28 A 60 A/CM2, EN CHAMP NUL ET A 77 K), ALORS QUE LA TEMPERATURE CRITIQUE DEMEURE INCHANGEE.

Détails

  • Titre original : STRUCTURE AND SUPERCONDUCTIVITY OF BISMUTH-(LEAD)-CALCIUM-STRONTIUM-COPPER-OXYGEN CERAMICS PROCESSED BY ARC MELTING.
  • Identifiant de la fiche : 1991-0524
  • Langues : Anglais
  • Source : J. Supercond. - vol. 2 - n. 4
  • Date d'édition : 12/1989
  • Document disponible en consultation à la bibliothèque du siège de l'IIF uniquement.

Liens


Voir d'autres articles du même numéro (4)
Voir la source

Indexation