Densité du courant critique des supraconducteurs filamentaires DyBa2Cu3O(y) produits par la fusion.

Transport critical current density of melt-processed filamentary DyBa2Cu3O(y) superconductors.

Auteurs : IKEBE Y., BAN E., MATSUOKA Y., et al.

Résumé

The authors studied the fabrication and characterization of filamentary Dy123 superconductors prepared by a solution spinning method. The precursor filament was partially-melted in flowing 1%O2+Ar and 20%O2+Ar at various temperature. It was found that Jc value at 77 K and self-field is significantly influenced by both partial melting temperature and atmosphere gas. The filamentary sample partially melted in 20%O2+Ar exhibited a dense microstructure and a fine dispersion of Dy211 particles.

Documents disponibles

Format PDF

Pages : 2006-3/ICMC-D5

Disponible

  • Prix public

    20 €

  • Prix membre*

    Gratuit

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : Transport critical current density of melt-processed filamentary DyBa2Cu3O(y) superconductors.
  • Identifiant de la fiche : 2008-1175
  • Langues : Anglais
  • Source : Multiconference CryoPrague 2006 (9th Cryogenics 2006, ICEC 21, ICMC'06)
  • Date d'édition : 17/07/2006

Liens


Voir d'autres communications du même compte rendu (142)
Voir le compte rendu de la conférence

Indexation