Effet du frittage sous haute pression sur les propriétés magnétiques et magnétocaloriques d'un composé Mn1.28Fe0.68P0.46Si0.58.

High-pressure sintering effect on the magnetic and magnetocaloric properties of Mn1.28Fe0.68P0.46Si0.58 compound.

Numéro : 1628

Auteurs : FAN W. D., OU Z. Q., HUANG G. F., et al.

Résumé

First-order phase transition material MnFePSi has attracted much attention as a room-temperature magnetic refrigerant. The influence of different applied pressure (2, 3 and 4 GPa) during sintering on the magnetic properties of MnFePSi compounds was investigated. All of the compounds crystallize in Fe2P-type hexagonal structure. The Curie temperature and thermal hysteresis decrease with increasing pressure. The compactness is enhanced when applying pressure upto 4 GPa, while the magnetic entropy change has hardly any change (pressure upto 3 GPa).

Documents disponibles

Format PDF

Pages : 2 p.

Disponible

  • Prix public

    10 €

  • Prix membre*

    7,50 €

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : High-pressure sintering effect on the magnetic and magnetocaloric properties of Mn1.28Fe0.68P0.46Si0.58 compound.
  • Identifiant de la fiche : 30012719
  • Langues : Anglais
  • Source : 6th International Conference on Magnetic Refrigeration at Room Temperature (Thermag VI). Proceedings: Victoria, Canada, September 7-10, 2014.
  • Date d'édition : 07/09/2014

Liens


Voir d'autres communications du même compte rendu (78)
Voir le compte rendu de la conférence

Indexation