Effet des paramètres de traitement sur une phase de formation 1:13 et propriétés magnétiques de composés de (La1-xCex)(Fe1-YMny)11.5Si1.5Hz.

The effect of processing parameters on 1:13 phase formation and magnetic properties of (La1-xCex)(Fe1-YMny)11.5Si1.5Hz compounds.

Numéro : 1538

Auteurs : SHI J., SUN Y., NI Z., et al.

Résumé

Large-scale preparation of La0.7Ce0.3Fe11.28Mn0.22Si1.5 compounds was investigated by melt-spinning technique. The microstructure of as-cast ribbon affects the 1:13 phase formation greatly in the annealing process: finer grains of as-cast ribbon accelerate 1:13 formation but lead to the growth of a-Fe grains in the annealing process. Homogeneous and stable La0.7Ce0.3Fe11.28Mn0.22Si1.5Hz is obtained after annealing ribbons under atmosphere of 0.2 MPa at 623 K for a week. After being kept for one year, there is almost no change in the Tc of the hydrides. Short preparation time, homogeneous and stable Tc, and large MCE suggest that large-scale (La1-xCex)(Fe1-yMny)11.5Si1.5Hz hydrides are promising candidates of magnetocaloric materials for practical magnetic refrigeration near room temperature.

Documents disponibles

Format PDF

Pages : 3 p.

Disponible

  • Prix public

    10 €

  • Prix membre*

    7,50 €

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : The effect of processing parameters on 1:13 phase formation and magnetic properties of (La1-xCex)(Fe1-YMny)11.5Si1.5Hz compounds.
  • Identifiant de la fiche : 30012720
  • Langues : Anglais
  • Source : 6th International Conference on Magnetic Refrigeration at Room Temperature (Thermag VI). Proceedings: Victoria, Canada, September 7-10, 2014.
  • Date d'édition : 07/09/2014

Liens


Voir d'autres communications du même compte rendu (78)
Voir le compte rendu de la conférence

Indexation