Étude de l'effet magnétocalorique dans des composés métalliques (Pr,Dy)2Fe17 et (Pr)2(Fe,Al)17.

Study of the magnetocaloric effect in (Pr,Dy)2Fe17 and (Pr)2(Fe,Al)17 intermetallic compounds.

Numéro : 1586

Auteurs : ZEHANI K., GUETARI R., LOBUE M., et al.

Résumé

The Pr2Fe17 compound is a potential candidate for low cost magnetocaloric materials with a significant relative cooling power (RCP) around room temperature (280 K). In this work, we present the results of the substitution of dysprosium for praseodymium and of the substitution of aluminum for iron in Pr2Fe17. The polycrystalline Pr2-xDyxFe17 (x = 0, 0.25) and Pr2Fe17-yAly (y = 0.25) were prepared by arc melting under a high purity argon and homogenized at 1373K to minimize the amount of other possible impurity phases. All the samples crystallize in the R3m of the rhombohedral Th2Zn17 type structure. The lattice parameter increases with the Al and Dy content. The Curie temperature increases with Dy content and Al content. The magnetic entropy change ?Sm was estimated from isothermal magnetization curves for all samples.

Documents disponibles

Format PDF

Pages : 2 p.

Disponible

  • Prix public

    10 €

  • Prix membre*

    7,50 €

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : Study of the magnetocaloric effect in (Pr,Dy)2Fe17 and (Pr)2(Fe,Al)17 intermetallic compounds.
  • Identifiant de la fiche : 30012777
  • Langues : Anglais
  • Source : 6th International Conference on Magnetic Refrigeration at Room Temperature (Thermag VI). Proceedings: Victoria, Canada, September 7-10, 2014.
  • Date d'édition : 07/09/2014

Liens


Voir d'autres communications du même compte rendu (78)
Voir le compte rendu de la conférence