Effet de la substitution de Nd sur les propriétés magnétocaloriques et la formation de phase 1:13 de La(FeCoSi)13 fritté.

Effect of Nd-substitution on the magnetocaloric properties and 1:13-phase formation of sintered La(FeCoSi)13.

Numéro : 1595

Auteurs : VIEYRA H. A., ZELLMANN V., BARCZA A., et al.

Résumé

The effects of partial substitution of La by Nd in La1-aNdaFe13-x-yCoySix alloys (0 = a = 0.12) are investigated. Our results suggest that the impact of Nd on the magnetocaloric properties correlates to the Co concentration. In Co-poor samples (y = 0.68), a reduction of the Curie temperature by –27.17°C/f.u.Nd, is observed. The addition of Nd, however, has no considerable improvement on the adiabatic temperature change. In contrast, the significance of Nd incorporation in Co-rich alloys (y = 1.03) is more evident. A stronger decrease in TC (–38.19°C/f.u.Nd) and a monotonic improvement up to 6% in the adiabatic temperature change are observed.

Documents disponibles

Format PDF

Pages : 2 p.

Disponible

  • Prix public

    10 €

  • Prix membre*

    7,50 €

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : Effect of Nd-substitution on the magnetocaloric properties and 1:13-phase formation of sintered La(FeCoSi)13.
  • Identifiant de la fiche : 30012885
  • Langues : Anglais
  • Source : 6th International Conference on Magnetic Refrigeration at Room Temperature (Thermag VI). Proceedings: Victoria, Canada, September 7-10, 2014.
  • Date d'édition : 07/09/2014

Liens


Voir d'autres communications du même compte rendu (78)
Voir le compte rendu de la conférence

Indexation