FISSURATION DES EPOXYDES PROVOQUEE PAR LA CONTRAINTE ET DEGAGEMENT D'ENERGIE A 4,2 K DANS LES FILS SUPRACONDUCTEURS REVETUS D'EPOXYDE.

STRESS-INDUCED EPOXY CRACKING AND ENERGY RELEASE AT 4.2 K IN EPOXY-COATED SUPERCONDUCTING WIRES.

Type d'article : Article

Résumé

ON A MESURE LES PICS DE TEMPERATURE PROVOQUES PAR FISSURATION DANS DES FILS D'ESSAI REVETUS D'EPOXYDE SOUS CONTRAINTE DE TENSION POUR ETUDIER LE SPECTRE D'ENERGIE DE FISSURES PROVOQUEES PAR CONTRAINTE DANS DES BOBINAGES D'AIMANTS SUPRACONDUCTEURS A DENSITE DE COURANT ELEVEE, IMPREGNES D'EPOXYDE. ON N'A PAS OBSERVE DE PICS DE TEMPERATURE PROVOQUANT DES FISSURES POUR DES CONTRAINTES DES FILS INFERIEURES A 180 MEGAPASCALS, NIVEAU QUI N'EST NORMALEMENT PAS DEPASSE POUR LES BOBINAGES D'AIMANTS SUPRACONDUCTEURS ATTEINTS DE FISSURES DE L'EPOXYDE. ON PRESENTE DES EXPLICATIONS POSSIBLES.

Détails

Titre original : STRESS-INDUCED EPOXY CRACKING AND ENERGY RELEASE AT 4.2 K IN EPOXY-COATED SUPERCONDUCTING WIRES.
Identifiant de la fiche : 1985-0924
Langues : Anglais
Source : Cryogenics - vol. 24 - n. 8
Date d'édition : 1984

Liens

Voir d'autres articles du même numéro (9)
Voir la source

Indexation

Thèmes : Supraconduction
Mots-clés : Aimant supraconducteur; Résine epoxy; Propriété mécanique; Supraconducteur