Partager

INFLUENCE D'UNE FORCE DE COMPRESSION TRANSVERSALE OU DE TENSION AXIALE SUR LA SUPRACONDUCTIVITE DE FILS DE PLOMB-MOLYBDENE(6)SOUFRE(8) ET D'ETAIN-MOLYBDENE(6) SOUFRE(8).

INFLUENCE OF TRANSVERSE COMPRESSIVE AND AXIAL TENSILE STRESS ON THE SUPERCONDUCTIVITY OF LEAD-MOLYBDENUM(6)SULPHUR(8) AND TIN-MOLYBDENUM(6)SULPHUR(8) WIRES.

Auteurs : GOLDACKER W.

Type d'article : Article

Résumé

C'EST LA PREMIERE FOIS QUE L'ON ETUDIE L'INFLUENCE D'UNE FORCE DE COMPRESSION TRANSVERSALE SUR CE TYPE DE COMPOSES. DE CES PREMIERS RESULTATS, ON PEUT CONCLURE QUE LES FILS MONOFILAMENTAIRES A PHASE DE CHEVREL, RENFORCES ACIER, PRESENTENT UNE BONNE STABILITE MECANIQUE ET UN BON COMPORTEMENT ELASTIQUE, QUI DEPENDENT FORTEMENT DU DEGRE DE RENFORCEMENT, DONC DE L'ETAT DE PRECONTRAINTE, DU FILAMENT. LA SENSIBILITE DU COURANT CRITIQUE ET DU CHAMP CRITIQUE SUPERIEUR, SOIT A UNE FORCE DE TENSION AXIALE, SOIT A UNE FORCE DE COMPRESSION TRANSVERSALE, EST BEAUCOUP PLUS PETITE QUE CELLE DES FILS DE NIOBIUM-ETAIN. CECI EST TRES PROMETTEUR POUR LES APPLICATIONS FUTURES DES FILS A PHASE DE CHEVREL EN CHAMP MAGNETIQUE INTENSE, TELLES QUE BOBINES D'INSERTION DES AIMANTS SUPRACONDUCTEURS OU BOBINES DE BITTER. DANS LES GRANDES BOBINES SUPRACONDUCTRICES, LES FORCES DE CONTRAINTE TRANSVERSALES PEUVENT ATTEINDRE DE 50 A 100 MEGAPASCALS.

Détails

  • Titre original : INFLUENCE OF TRANSVERSE COMPRESSIVE AND AXIAL TENSILE STRESS ON THE SUPERCONDUCTIVITY OF LEAD-MOLYBDENUM(6)SULPHUR(8) AND TIN-MOLYBDENUM(6)SULPHUR(8) WIRES.
  • Identifiant de la fiche : 1990-2258
  • Langues : Anglais
  • Source : Cryogenics - vol. 29 - n. 10
  • Date d'édition : 1989