Nucléation de fissures assistée par l'environnement dans les matériaux magnétocaloriques à base de La(Fe,Mn,Si)13.

Environment-assisted crack nucleation in La(Fe,Mn,Si)13-based magnetocaloric materials.

Auteurs : WANG S., LOVELL E., GUO L., WILSON N., RYAN M. P., GIULIANI F.

Type d'article : Article de la RIF

Résumé

Cracking in La(Fe,Si)13-based magnetocaloric materials has been observed to predominantly form around La-rich (La2O3) particles and pose a threat to their long-term structural integrity. To understand the formation of these cracks, FIB cross-sectional polishing followed by SEM characterisation was employed to study local microstructural evolution after air exposure. Results suggest that volume expansion and internal degradation associated with a chemical reaction between La2O3 particles and water/moisture can lead to crack nucleation in the 1:13 phase adjacent to La-rich particles. This observation indicates that the formation of La-rich particles should be suppressed, or their size minimised during material processing to ensure the long-term structural integrity of La(Fe,Mn,Si)13 magnetocaloric materials.

Documents disponibles

Format PDF

Pages : 1-4

Disponible

  • Prix public

    20 €

  • Prix membre*

    Gratuit

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : Environment-assisted crack nucleation in La(Fe,Mn,Si)13-based magnetocaloric materials.
  • Identifiant de la fiche : 30029383
  • Langues : Anglais
  • Sujet : Technologie
  • Source : International Journal of Refrigeration - Revue Internationale du Froid - vol. 135
  • Date d'édition : 03/2022
  • DOI : http://dx.doi.org/10.1016/j.ijrefrig.2021.12.016
  • Document disponible en consultation à la bibliothèque du siège de l'IIF uniquement.

Liens


Voir d'autres articles du même numéro (26)
Voir la source

Indexation