RELATION ENTRE QUALITE DE CROISSANCE ET DENSITE DE COURANT CRITIQUE, POUR DES COUCHES MINCES D'YBCO OBTENUES PAR PULVERISATION.

GROWTH QUALITY AND CRITICAL CURRENT DENSITY OF SPUTTERED YBCO THIN FILMS.

Auteurs : SCHAUER W.

Type d'article : Article

Résumé

DES COUCHES MINCES D'YBCO ONT ETE OBTENUES PAR DEPOT SUR DES SUBSTRATS MONOCRISTALLINS (ALUMINE, OXYDE DE MAGNESIUM, OXYDE MIXTE DE STRONTIUM ET DE TITANE, ZIRCONE). LES VALEURS MAXIMALES DE DENSITE DE COURANT CRITIQUE MESUREES, EN CHAMP NUL ET A 77 K, SONT, POUR LES COUCHES SUR OXYDE DE STRONTIUM/TITANE, OXYDE DE ZIRCONIUM, OXYDE DE MAGNESIUM, RESPECTIVEMENT DE 5.000.000, 2.000.000 ET 900.000 A/CM2. LES FILMS PREPARES SUR ALUMINE ET ZIRCONE ORIENTEES AU HASARD SONT ESSENTIELLEMENT POLYCRISTALLINS, CE QUI ENTRAINE UNE DIMINUTION DES VALEURS DE LA DENSITE DE COURANT CRITIQUE. LES VALEURS DE LA DENSITE DE COURANT CRITIQUE AUGMENTENT (JUSQU'A ATTEINDRE 2. 000.000 A/CM2, A 77 K) LORSQUE L'EPAISSEUR DU FILM DECROIT. POUR LES FILMS ULTRAMINCES (D = 5 NM), LA DENSITE DE COURANT CRITIQUE S'EFFONDRE (350.000 A/CM2 A 4,2 K) MAIS SA VARIATION AVEC LE CHAMP MAGNETIQUEEST TOTALEMENT DIFFERENTE DE CELLE DES FILMS EPAIS.

Détails

  • Titre original : GROWTH QUALITY AND CRITICAL CURRENT DENSITY OF SPUTTERED YBCO THIN FILMS.
  • Identifiant de la fiche : 1991-1954
  • Langues : Anglais
  • Source : Cryogenics - vol. 30 - n. 7
  • Date d'édition : 1990

Liens


Voir d'autres articles du même numéro (13)
Voir la source

Indexation