REPRODUCTIBILITE DES MESURES DE TEMPERATURE DE TRANSITION ET DE DENSITE DE COURANT CRITIQUE FAITES SUR DES COUCHES MINCES D'YBCO DEPOSEES SUR OXYDE MIXTE DE LANTHANE ET D'ALUMINIUM.

REPRODUCIBILITY OF TRANSITION TEMPERATURE AND CRITICAL CURRENT DENSITY OF THIN FILMS OF YBCO ON LANTHANUM-ALUMINIUM MIXED OXIDE.

Auteurs : MOGRO-CAMPERO A., TURNER L. G.

Type d'article : Article

Résumé

LA TEMPERATURE CRITIQUE DE SUPRACONDUCTION EST ELEVEE (89 OU 90 K) LORSQUE LA COMPOSITION DE LA COUCHE MINCE CORRESPOND A UNE PHASE PURE (BARYUM/YTTRIUM = 2, CUIVRE/YTTRIUM = 3) OU A UNE PHASE ENRICHIE EN BARYUM ET CUIVRE. DANS CES CAS, LA DENSITE DE COURANT CRITIQUE A 77 K A UNE VALEUR MOYENNE DE 200.000 A/CM2 ET TEND A DECROITRE LORSQUE L'EPAISSEUR DE LA COUCHE MINCE CROIT (DE 0,2 A 0,8 MICROMETRES). LES VARIATIONS DE LA DENSITE DE COURANT CRITIQUE NE SONT PAS LIEES AUX ECARTS A LA STOECHIOMETRIE PARFAITE. L'AUGMENTATION DE LA PENTE DES COURBES RESISTANCE-TEMPERATURE, A TEMPERATURE SUPERIEURE A 100 K, ET LES FAIBLES VALEURS DE LA RESISTIVITE A TEMPERATURE AMBIANTE SEMBLENT LIEES AUX FORTES VALEURS DE DENSITE DE COURANT CRITIQUE. SI L'ON AUGMENTE LA PROPORTION DE L'YTTRIUM PAR RAPPORT AU BARYUM ET AU CUIVRE, LA TEMPERATURE DE TRANSITION BAISSE DE PLUSIEURS DEGRES.

Détails

  • Titre original : REPRODUCIBILITY OF TRANSITION TEMPERATURE AND CRITICAL CURRENT DENSITY OF THIN FILMS OF YBCO ON LANTHANUM-ALUMINIUM MIXED OXIDE.
  • Identifiant de la fiche : 1992-0965
  • Langues : Anglais
  • Source : J. Supercond. - vol. 4 - n. 1
  • Date d'édition : 02/1991
  • Document disponible en consultation à la bibliothèque du siège de l'IIF uniquement.

Liens


Voir d'autres articles du même numéro (4)
Voir la source

Indexation