Transformation Martensitique dans du SUS 304L et 316L pendant des tests de tension à basses températures.

Martensitic transformation in SUS 304L and 316L during tensile tests at low temperatures.

Auteurs : OGATA T., YURI T., ONO Y.

Résumé

Changes of ferrite content of SUS 304L and SUS 316L during tensile tests were measured at room temperature to 4 K. The tensile tests were carried out in the helium gas environment below 77 K and in cooled alcohol above 190 K. The ferrite content was measured by ferrite scope at the specified strain. For SUS 304L, the amount of ferrite content increased with decreasing temperature down to 233 K, and it increased little below 233 K. At room temperature, it increased steeply after 20% plastic strain. For SUS 316L, it increased with decreasing temperature down to 4 K, it increased steeply after 60% plastic strain above 243 K.

Documents disponibles

Format PDF

Pages : 2006-3/ICMC-D1

Disponible

  • Prix public

    20 €

  • Prix membre*

    Gratuit

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : Martensitic transformation in SUS 304L and 316L during tensile tests at low temperatures.
  • Identifiant de la fiche : 2008-1087
  • Langues : Anglais
  • Source : Multiconference CryoPrague 2006 (9th Cryogenics 2006, ICEC 21, ICMC'06)
  • Date d'édition : 17/07/2006

Liens


Voir d'autres communications du même compte rendu (142)
Voir le compte rendu de la conférence

Indexation