Résumé
The corrosion behaviour of LaFe(13-x)Si(x) alloys were studied in this paper. The materials were prepared by arc melting and annealed at 1623 K for 3 h. X-ray diffraction and scanning electron microscope (SEM) show that the. NaZn(13) type phase is the main phase, alpha-Fe is present in form of globular grains while the LaFeSi phase is distributed along the grain boundaries of the main phase. The SEM shows that the phase containing more lanthanum corrodes faster than other phases. La(2)[CO(3)]3-H(2)O(8) was formed due to the existence of CO2 in the solution in the open system, and Fe(OH)3 was deposited on the bottom of bottle after 168 h immersion. H2C2O4 and NaOH were used to adjust the pH value, and the result show that the corrosion current of LaFe(11.6)Si(1.4) alloy in alkaline solution is smaller than that in acid solution.
Documents disponibles
Format PDF
Pages : 2009-3
Disponible
Prix public
20 €
Prix membre*
Gratuit
* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)
Détails
- Titre original : Corrosion behaviour of LaFe(13-x)Si(x) system compounds.
- Identifiant de la fiche : 2009-1627
- Langues : Anglais
- Source : 3rd International Conference on Magnetic Refrigeration at Room Temperature
- Date d'édition : 11/05/2009
Liens
Voir d'autres communications du même compte rendu (67)
Voir le compte rendu de la conférence
Indexation
-
Thèmes :
Circulation du fluide : tuyauterie, régulation, automatisme, sécurité;
Froid calorique (froid magnétocalorique, électrocalorique, élastocalorique et barocalorique);
Autres systèmes de production de froid (dessiccation, thermoélectricité, thermoacoustique...) - Mots-clés : Propriété mécanique; Réfrigerateur magnétique; Lanthane; Alliage; Silicium; Matériau; Fer; Corrosion
-
On the existence of a ternary liquid miscibilit...
- Auteurs : ROCCO D. L., GAMA S., COELHO A. A., et al.
- Date : 11/05/2009
- Langues : Anglais
- Source : 3rd International Conference on Magnetic Refrigeration at Room Temperature
- Formats : PDF
Voir la fiche
-
Magnetocaloric effect and properties of La[Fe(1...
- Auteurs : HUANG J. H., TAKATA H., LIU C. L., et al.
- Date : 11/05/2009
- Langues : Anglais
- Source : 3rd International Conference on Magnetic Refrigeration at Room Temperature
- Formats : PDF
Voir la fiche
-
Phase structure and magnetocaloric effect of sh...
- Auteurs : LIU T., CHEN Y. G., TANG Y. B., et al.
- Date : 11/05/2009
- Langues : Anglais
- Source : 3rd International Conference on Magnetic Refrigeration at Room Temperature
- Formats : PDF
Voir la fiche
-
Advantage of the itinerant electron metamagneti...
- Auteurs : FUJITA A., FUJIEDA S., FUKAMICHI K.
- Date : 11/05/2009
- Langues : Anglais
- Source : 3rd International Conference on Magnetic Refrigeration at Room Temperature
- Formats : PDF
Voir la fiche
-
Hydrogen absorption kinetics and hydrogen desor...
- Auteurs : ZHANG E., CHEN Y., TANG Y., et al.
- Date : 11/05/2009
- Langues : Anglais
- Source : 3rd International Conference on Magnetic Refrigeration at Room Temperature
- Formats : PDF
Voir la fiche