Structure de phase et effet magnétocalorique de composés d'un système au LaFe(13-x)Si(x) recuits rapidement à basse température.

Phase structure and magnetocaloric effect of short high temperature annealed LaFe(13-x)Si(x) system compounds.

Auteurs : LIU T., CHEN Y. G., TANG Y. B., et al.

Résumé

In this study, phase formation with NaZn(13)-type structure of LaFe(13-x)Si(x) system compounds (x= 1.1, 1.2, 1.3, 1.4, 1.5) by high-temperature annealing at 1573 K for 1 hour have been investigated. The results demonstrate that coarse dendrites are observed in the microstructure of as-cast LaFe(13-x)Si(x) samples and 1:13 phase is formed after short high temperature annealing. The magnetic entropy change of 17.56 J/kg.K for LaFe(11.6)Si(1.4) was obtained at Tc=190 K under the magnetic field changes of 0 to about 5 T.

Documents disponibles

Format PDF

Pages : 2009-3

Disponible

  • Prix public

    20 €

  • Prix membre*

    Gratuit

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : Phase structure and magnetocaloric effect of short high temperature annealed LaFe(13-x)Si(x) system compounds.
  • Identifiant de la fiche : 2009-1606
  • Langues : Anglais
  • Source : 3rd International Conference on Magnetic Refrigeration at Room Temperature
  • Date d'édition : 11/05/2009

Liens


Voir d'autres communications du même compte rendu (67)
Voir le compte rendu de la conférence

Indexation