Comportements lors de l'hydrogénation haute température et propriétés magnétocaloriques du composé LaFe11.6Si1.4.

High-temperature hydrogenation behaviors and magnetocaloric properties of LaFe11.6Si1.4 compound.

Numéro : pap. 134

Auteurs : TANG Y., CHEN Y., ZHENG H., et al.

Résumé

LaFe11.6Si1.4 samples were hydrogenated at the initial hydrogen-filling pressure of 0.6 MPa and different temperatures (from 393 K to 478 K). The hydrogen absorption kinetics performance, magnetocaloric effect and Curie temperature (TC) of these alloys were investigated. The results show that all samples have excellent hydrogen absorption kinetics performance and the hydrogen saturation time of these samples decreased from 45 min (at 393 K) to 4 min (at 478 K).The magnetic entropy changes were 16.27 J/kg.K (before hydrogen absorption), 12.2 J/kg.K (at 393K), 10.48 J/kg.K (at 423K), 7.81 J/kg.K (at 453) and 10.64 J/kg.K(at478K,respectively. The Curie temperature varied from 325.7Kfor an absorption temperature of 393Kto 276.8Kfor an absorption temperature of 478K.

Documents disponibles

Format PDF

Pages : 4 p.

Disponible

  • Prix public

    20 €

  • Prix membre*

    Gratuit

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : High-temperature hydrogenation behaviors and magnetocaloric properties of LaFe11.6Si1.4 compound.
  • Identifiant de la fiche : 30019378
  • Langues : Anglais
  • Source : 7th International Conference on Magnetic Refrigeration at Room Temperature (Thermag VII). Proceedings: Turin, Italy, September 11-14, 2016.
  • Date d'édition : 11/09/2016
  • DOI : http://dx.doi.org/10.18462/iir.thermag.2016.0134

Liens


Voir d'autres communications du même compte rendu (71)
Voir le compte rendu de la conférence

Indexation