Dehydration and hydration reactivity of La-based mixed hydroxides for chemical heat storage.

Numéro : pap. n. 31

Auteurs : RYU J., ISHITOBI H., KATO Y.

Résumé

The dehydration and hydration behavior of La-based mixed hydroxides were studied to develop a new material for chemical heat storage. It was demonstrated that the dehydration of La-based mixed hydroxides proceeded at around 300°C, which was lower than that in the case of authentic lanthanum hydroxide. These hydroxides showed higher hydration reactivity than lanthanum oxy-hydroxide (LaOOH), under hydration at 110°C with 7.4 kPa of water vapor after dehydration at 300°C. The heat output capacity of La0.50Y0.50(OH)3 was estimated as 282 kJ kg-1 after dehydration at 300°C. These results indicate that La-based mixed hydroxides are suitable for the utilization of industrial waste heat at around 300°C.

Documents disponibles

Format PDF

Pages : 9 p.

Disponible

  • Prix public

    20 €

  • Prix membre*

    15 €

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : Dehydration and hydration reactivity of La-based mixed hydroxides for chemical heat storage.
  • Identifiant de la fiche : 30014420
  • Langues : Anglais
  • Source : International sorption heat pump conference (ISHPC2014), College Park, United States, March 31-April 2, 2014.
  • Date d'édition : 02/03/2014

Liens


Voir d'autres communications du même compte rendu (125)
Voir le compte rendu de la conférence

Indexation