Important changement d'entropie magnétique des composés La(1,2)Fe(11,6)Si(1,4).

Large magnetic entropy change in La(1.2)Fe(11.6)Si(1.4) compounds.

Auteurs : LI F. A., SONG L., XIE G. Q., et al.

Résumé

By adding an extra amount of La to the LaFe(11.6)Si(1.4) compound, the authors found that the stable NaZn13 cubic structure phase (space group is Fm-3c) can be more easily obtained by annealing at 1100°C for 50 hours. Simultaneously, a small amount of La-rich phase and the alpha-Fe phase are found. A clear itinerant electron metamagnetic transition and large magnetic entropy change have been observed in the compound. The peak values of magnetic entropy change is 48 J/kg.K under a magnetic field change from 0 to 1.5 T.

Documents disponibles

Format PDF

Pages : 2010-4

Disponible

  • Prix public

    20 €

  • Prix membre*

    Gratuit

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : Large magnetic entropy change in La(1.2)Fe(11.6)Si(1.4) compounds.
  • Identifiant de la fiche : 2011-0166
  • Langues : Anglais
  • Source : 4th International Conference on Magnetic Refrigeration at Room Temperature (Thermag IV). Proceedings: Baotou, China, August 23-27, 2010.
  • Date d'édition : 23/08/2010

Liens


Voir d'autres communications du même compte rendu (54)
Voir le compte rendu de la conférence

Indexation