Nucléation des matériaux à changement de phase dans les géométries confinées.

Nucleation of PCMs in confined geometries.

Numéro : pap. 2

Auteurs : HAGELSTEIN G., GSCHWANDER S.

Résumé

This work investigates the influence of particle size on crystallization behaviour of microencapsulated and emulsified n-octadecane using differential scanning calorimetry (DSC) and laser diffraction. Analyses of microcapsules show a stepwise decrease of nucleation temperature (from 26 °C to 14 °C) with decreasing particle size (from 300 µm to 3 µm). Further reduction of particle size in emulsions (< 0.2 µm) results in a slight decrease of nucleation temperature (<2 K). Analyses of cooling thermograms of emulsions show two peaks, a minor peak around 8-9 °C and a major peak, which onset nucleation temperature Tc is influenced substantially by the lipophilic character of the surfactants (Tc varies between 13 °C and 22 °C).
The minor peak is attributed to the transition from rotator to stable crystal phase and its signal increases with decreasing particle size.

Documents disponibles

Format PDF

Pages : 8

Disponible

  • Prix public

    20 €

  • Prix membre*

    Gratuit

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : Nucleation of PCMs in confined geometries.
  • Identifiant de la fiche : 30017863
  • Langues : Anglais
  • Source : 11th IIR Conference on Phase-Change Materials and Slurries for Refrigeration and Air Conditioning. Proceedings: Karlsruhe, Germany, May 18-20, 2016.
  • Date d'édition : 18/05/2016
  • DOI : http://dx.doi.org/10.18462/iir.pcm.2016.0002

Liens


Voir d'autres communications du même compte rendu (31)
Voir le compte rendu de la conférence

Indexation