Etude expérimentale sur la minimisation de la formation de givre sur une surface froide en convection naturelle à l'aide d'une peinture anti-givre innovante. I. Performance en tant qu'agent anti-givre et comparaison avec une surface métallique non traitée.

An experimental study on minimizing frost deposition on a cold surface under natural convection conditions by use of a novel anti-frosting paint. I. Anti-frosting performance and comparison with the uncoated metallic surface.

Auteurs : LIU Z. L., WANG H. Y., ZHANG X. H., et al.

Type d'article : Article, Article de la RIF

Résumé

In this study, an experimental investigation is made of the anti-frosting performance of the authors' newly developed anti-frosting paint. By coating the paint on a cold metal surface, the onset of the frost formation may be delayed at least 15 min and the thickness of the deposited frost layer may be reduced by at least 40% and thus the weight of the deposited frost may be reduced by more than 40% compared with that on the uncoated copper surface. Under some preferable conditions (air relative humidity less than 60%, cold plate surface temperature higher than -10°C), the coating surface can be kept free of frost at least for 3 h. (See also this Bulletin, reference 2006-1244.)

Documents disponibles

Format PDF

Pages : 229-236

Disponible

  • Prix public

    20 €

  • Prix membre*

    Gratuit

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : An experimental study on minimizing frost deposition on a cold surface under natural convection conditions by use of a novel anti-frosting paint. I. Anti-frosting performance and comparison with the uncoated metallic surface.
  • Identifiant de la fiche : 2006-1243
  • Langues : Anglais
  • Source : International Journal of Refrigeration - Revue Internationale du Froid - vol. 29 - n. 2
  • Date d'édition : 03/2006

Liens


Voir d'autres articles du même numéro (17)
Voir la source