Recherche sur l'effet magnétocalorique d'alliages de LaFe(11.17-x)Co(0.78)Si(1.05)B(x).

Research on the magnetocaloric effect of LaFe(11.17-x)Co(0.78)Si(1.05)B(x) alloys.

Auteurs : HUANG J. H., SONG L., JIN P. Y., et al.

Résumé

The authors have studied the magnetocaloric effect near room temperature of these alloys using commercial pure material. The element B is interstitial atom. The phase transition temperature increased from 277 K when x= 0 to 289 K when x= 0.3 with the increasing content of element B. Moreover, the magnetic entropy change and the adiabatic temperature change which was directly measured also increased with the increasing content of B. And the alloy showed the large magnetocaloric effect at lower magnetic field. The measurements indicated that both thermal hysteresis and hysteresis are rather small.

Documents disponibles

Format PDF

Pages : 2007-1

Disponible

  • Prix public

    20 €

  • Prix membre*

    Gratuit

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : Research on the magnetocaloric effect of LaFe(11.17-x)Co(0.78)Si(1.05)B(x) alloys.
  • Identifiant de la fiche : 2007-1585
  • Langues : Anglais
  • Source : 2nd International Conference on Magnetic Refrigeration at Room Temperature
  • Date d'édition : 11/04/2007

Liens


Voir d'autres communications du même compte rendu (48)
Voir le compte rendu de la conférence

Indexation