Comportement en termes de corrosion d'un alliage de LaFe11.6Si1.4 dans des solutions aqueuses inorganique et organique.

The corrosion behaviour of LaFe11.6Si1.4 alloy in inorganic and organic water solution.

Numéro : sect. 2

Auteurs : TANG Y., CHEN Y., ZHANG E.

Résumé

The corrosion behavior of LaFe11.6Si1.4 alloy was investigated in Na2WO4 water solution and benzotriazole/sodium benzoate mixed solution by electrochemical measurements. The results show that the corrosion was inhibited by Na2WO4 solution. The high inhibition effect was due to the slow anodic dissolved reaction and the low diffusion at low concentration of inhibitor. While in benzotriazole/sodium benzoate mixed solution, the inhibition efficiency was influenced seriously by the concentration of benzotriazole and pH value. The high concentration benzotriazole was advantaged to form a compact oxidation layer and prevent the dissolution of Fe.

Documents disponibles

Format PDF

Pages : 187-192

Disponible

  • Prix public

    20 €

  • Prix membre*

    Gratuit

* meilleur tarif applicable selon le type d'adhésion (voir le détail des avantages des adhésions individuelles et collectives)

Détails

  • Titre original : The corrosion behaviour of LaFe11.6Si1.4 alloy in inorganic and organic water solution.
  • Identifiant de la fiche : 30005515
  • Langues : Anglais
  • Source : 5th International Conference on Magnetic Refrigeration at Room Temperature (Thermag V). Proceedings: Grenoble, France, September 17-20, 2012.
  • Date d'édition : 17/09/2012

Liens


Voir d'autres communications du même compte rendu (70)
Voir le compte rendu de la conférence

Indexation