LIQUID PHASE PREPARATION OF BSCCO FILM STRUCTURES.

Author(s) : KOSMYNA M. B.

Type of article: Article

Summary

TEXTURED BSCCO FILMS WERE GROWN FROM A SOLUTION-MELT WITH 10-30 WT% BSCCO AND 70-90 WT% POTASSIUM CHLORIDE. THE SUBSTRATES WERE OF YTTRIUM-ALUMINIUM-OXIDE(3) OF THE ORIENTAT THE FILMS CONSISTED OF CRYSTALLITES OF UP TO 300 MICROMETERS IN SIZE, ORDERED INTO GRAINS, AND THEIR C-AXIS WAS PERPENDICULAR TO THE SUBSTRATE PLANE. THE FILMS HAD ZERO RESISTANCE AT 82-85 K, AND THE CRITICAL CURRENT DENSITY WAS 100 A/CM2 AT 77 K.